THE CATALYST OF ALUMINA-NICKEL-MOLYBDENE “ChKG-09”

KSt 6.3-112:2012 (CN of FEA code 381 519 9000)

The catalyst «ChKG-09» is designed for sulfide compounds hydrogenization process from hydrocarbon in ammonia production, for auxiliaries.

The catalyst consists of hydroxide aluminum re –precipitation, ammonium molybdate, nitric-acid nickel and produced in the forms of extrudates with greenish coloring.

Specifications
Physical configuration	Extrudates with greenish coloring
Size of granules, mm - outer diameter - length	5,0-6,0 5,0-20,0
Bulk density, kg/dm3, within	0,6±0,7
Mechanical strength – breaking force at squeezing along generatrix, MPa, - average - minimum	3,0 1,5
Mass fraction of wastage while transfixion	under 600 ºС- no more than 5,0
Mass fraction of active components, % nickel oxide, within molybdenum trioxide	2,5-4,0 11,0-14,0
Strength index on breaking, kg/mm diameter of granule, no less than average	0,8
Activity of catalyst in hydrogenolysis of butylene-alkyl hydrosulphide under300 оС and rate of volume flow 300 h-1, %, no less than h	92

Safety requirements: in accordance with regulations.

Packaging: in clean, dry, non-deformable in transit, tightly closed steel barrels, welded, under State Standard 6247, with capacity of 200 dm³ or in drums of type (50÷100) dm³ State Standard 5044 and in special containers with capacity of 40 dm³.

Transportation: by all modes of closed transport in accordance with traffic activity regulations. The wagon loading is carried out until gross tonnage or weight-carrying capacity during car freight.

Storage: Drums with catalysts must be held in dry, clean building separate from volatile chemical products in tightly closed containers.